Bearing a half-open and closed types, common failure modes commonly known as "lap", mainly bearing outer ring and bore friction and wear caused by friction with the 2311 Putty (ultra-smooth metal TM), 2215 wear Putty (titanium TM) so you can easily restore the bearing hole size.
Semi-open type bearing bore repair
(1) Surface treatment: the best polished surface to be repaired fork grooves transaction, pay attention to keep the hole on both sides of the bearing is not worn on the surface of the circumferential direction as the positioning of the mold surface.
(2) Degreasing: the new 1755 season with a cleaning agent can be strictly clean surface oil.
(3) Processing of mold, including: die diameter = diameter of the bearing outer ring; die length (L) is greater than the hole width of 20 ~ 40mm; roughness of the original bearing design requirements shall prevail.
(4) Processed on a thin coat of mold can match the new 1731 release agent.
(5) Preparation of putty, and coating the top and bottom polished clean good place to be repaired, leaving a sufficient margin.
(6) Will be placed in the mold half of the bearing seat, compaction, clean up the spilled glue.
(7) Putty good painted on the box labeled, with the locking bolt by assembly requirements. Putty curing in the overflow of excess material before wipe.
(8) Cured 8 to 16 hours (25 ℃ when), the open bolt, remove the mold



Other News:
Common extrusion methods
The size of bearing components and parts
Half-open type bearing repair process
Tolerances associated with the bearing size
Extend bearing service life cycle method
Several factors affect the service life of plate mill backup roll bearings
The advantages of linear motion bearings and uses
Roller bearing repair steps