Bearing collar after heat treatment deformation of the situation can be roughly divided into three types: the first kind is diameter changes (Vpe), the second average diameter changes (Vdmp), the third class for flatness changes (Ape), these three categories of deformation often overlapping, of which the most easy generation diameter change, and change large amount, so to control deformation quenching, main is to try to reduce the diameter of the collar of change.

bearing

First the ring deformation of quenching factors

A, bearing steel structure defects and annealing after the original cause the organization of uneven distribution of carbide size, will lead to quenching deformation.

B, quenching heat stress and organization when the greater the stress, the greater the quenching deformation. The thermal stress and organizational force includes: the heating temperature, heating speed and uniformity, the cooling speed and uniformity, cooling medium temperature, etc.

C, ring throwing, car process residual stress size, and the diameter of the car after processing by the size of the change, and hardened to the quantity of the change, and in the direction of the basic agreement.

Second, reduce the deformation of quenching collar measures

A, strictly control the cooling speed, improve the quality of annealing. Ball annealing cooling speed size, directly affecting the carbide shapes, sizes and dispersion, thereby affecting the quenching and tempering technology formulating, diameter changes quantity, and eventually mechanics performance. So in the correct formulation annealing process at the same time, the cooling speed strictly control in 10 ~ 25 ℃ / h, for the heat treatment to make organization.

B, strict KongZhiChe processing contractor changes, from table 2-63 can see, after turning the diameter of the change and quenching deformation closely related. The greater the amount car machining diameter changes, the hardening of large diameter changes also about, and in the direction of the basic to remain consistent. So to control the diameter of the quench heating changes, the first to strictly control lathe work process diameter changes.

 
C, meet each other in hardness and organization premise, quench heating try to take lower limit temperature, the temperature control of the three points appropriate reduction furnace caterpillar area first temperature, extend the heating time to slow down the heating speed, ensure that contractor is heated evenly, reduce quenching diameter changes.



Other News:
To select the most suitable heart bearing clearance of work is bearing clearance
Common NSK bearing failures analytical
Reduce ring quenching deformation
Used for newspaper printing roller bearing damage judgment
The bearing outer ring can be separable out
In the interior of the contact point lubricant friction and lubricant mixing and
TIMKEN bearing can effectively improve the groove shape error
Import bearing monomer clearance determination